Fabricante de tubos de acero inoxidable 904L en China
- UNS N08904
- ES X1NiCrMoCu25-20-5
- DIN / W.Nr. 1.4539
- JIS SUS 890L
- AFNOR Z2 NCDU 25-20
- ASTM A312 / ASME SA312
- ASTM A213
- ASTM B677
- EN 10216-5
- EN 10217-7
Composición química de los tubos de acero inoxidable 904L
| Ni | Cr | Mes | Cu | Minnesota | Si | C | P | S | Fe |
|---|---|---|---|---|---|---|---|---|---|
| 23.00% - 28.00% | 19.00% - 23.00% | 4,00% - 5,00% | 1,00% - 2,00% | ≤ 2.0% | ≤ 1.00% | ≤ 0,020% | ≤ 0,045% | ≤ 0,035% | Equilibrio |
Elementos clave de aleación
El alto contenido de níquel y cromo no sólo estabiliza la microestructura austenítica, sino que también proporciona al tubo una base muy resistente contra diversos ácidos orgánicos e inorgánicos. Previene eficazmente la SCC.
Aumenta significativamente la resistencia del material a la corrosión por picaduras y grietas en ambientes marinos o soluciones de alta concentración de cloruros.
La adición de cobre mejora enormemente la resistencia a la corrosión del material en ambientes reductores,especialmente en ácido sulfúrico diluido,así como en ácidos fosfórico y acético.
El contenido extremadamente bajo de carbono impide la precipitación de carburos de cromo en los límites de grano durante la soldadura o el tratamiento térmico, eliminando así por completo el riesgo de corrosión intergranular.
¿Tiene alguna necesidad?
Más información
Propiedades mecánicas de los tubos de acero inoxidable 904L
| Fuerza de Tensión | Fuerza de producción | Alargamiento | Dureza |
|---|---|---|---|
| ≥ 490 MPa (71 ksi) | ≥ 220 MPa (32 ksi) | ≥ 35% | ≤ 90 HRB (180 HBW) |
Propiedades mecánicas clave
Como acero inoxidable súper austenítico, el 904L ofrece un alargamiento superior a 40%, lo que significa que incluso cuando se somete a impactos externos, flexiones severas o trabajo en frío, la tubería mantiene un margen de seguridad extremadamente alto contra la fractura.
El 904L no sufre una transición frágil ni siquiera a temperaturas extremadamente bajas, lo que lo hace ideal para sistemas de tuberías industriales especializados en medios criogénicos.
Aunque la resistencia del 904L es ligeramente superior a la del 316L estándar,mantiene una dureza moderada.La tubería es fácil de doblar en frío,abocardar y mecanizar durante la instalación real.
Tratamiento térmico de los tubos de acero inoxidable 904L
Recocido de soluciones
Aliviar el estrés
Está estrictamente prohibido mantener o enfriar lentamente 904L en el rango de 450°C - 850°C, ya que este es el rango de temperatura en el que las fases frágiles son propensas a la precipitación.
Tratamiento térmico posterior a la soldadura
Decapado y pasivado
Nuestras capacidades en relación con los tubos de acero inoxidable 904L
Amplias capacidades de fabricación y suministro
Tubos sin soldadura
- Gama de especificaciones:
1/2″ - 24″
SCH10S, SCH20, SCH40S/STD, SCH80S/XS, SCH30, SCH60, SCH80, SCH100, SCH120, SCH160, XXS - Process Advantages:
Utilizing multi-pass cold drawing/cold rolling technology ensures exceptional uniformity in wall thickness and excellent inner surface finish.
Tubos soldados
- Gama de especificaciones:
1/2″ – 104″
SCH5S~80S/XS - Process Advantages:
We utilize fully automated TIG or plasma welding,combined with in-line solution treatment of the weld,to ensure that the grain size of the weld matches that of the base material exactly.
We strictly comply with international standards such as ASTM A312, ASTM A213, ASTM A269, ASME SA312, and EN 10216-5.
Advanced Heat Treatment and Surface Control
Equipped with advanced continuous atmosphere furnaces,the material is heated to 1100°C–1150°C and then rapidly quenched in water within seconds,thoroughly preventing the precipitation of σ-brittle phases and fully restoring the material’s resistance to acid and pitting corrosion.
We operate a fully automated pickling line that performs rigorous nitric acid-hydrofluoric acid cleaning after heat treatment,forming a dense,chromium- and molybdenum-rich passivation film on the pipe surface.
We offer bright annealed surfaces,mechanical polishing,and electropolished pipes for the pharmaceutical and semiconductor industries.
Advanced Customization And Secondary Processing Capabilities
Stringent Quality Assurance And 100% Inspection System
100% eddy current testing (ET) and ultrasonic testing (UT) are performed;welded pipes undergo additional 100% radiographic testing (RT) as well as air tightness and hydrostatic pressure tests.
100% material inspection is conducted using original imported handheld and benchtop PMI (spectrometers);Intergranular corrosion testing (ASTM A262 Practice E) and metallographic examination are performed on every batch.
We fully cooperate with third-party organizations such as SGS, TÜV, BV, and DNV for factory supervision and pre-shipment sampling inspections,and provide original Material Test Certificates (MTCs) compliant with EN 10204 3.1 or 3.2.
Applications of 904L Stainless Steel Pipe
- Phosphoric Acid & Fertilizer Industry
- Marine Engineering & Subsea Manifolds
- Desalination & Reverse Osmosis
- Petroleum Refining & Hydrocracking
- Producción de ácido sulfúrico
- Acetic Acid & Fine Chemical Processing
- Nuclear & Conventional Power Generation
- Desulfuración de gases de combustión
- Pulp and Paper Bleaching
- Fabricación farmacéutica
FAQs About 904L Stainless Steel Pipe
904L contiene niveles más altos de níquel y molibdeno,con la adición de copper.While Tubos de acero inoxidable 316L son muy susceptibles a la corrosión por picaduras y a la corrosión general cuando se exponen al agua de mar y al ácido sulfúrico diluido,el 904L presenta una resistencia excepcional a la corrosión en ambientes cálidos,ácido sulfúrico concentrado,ácido fosfórico y ambientes marinos.
El coste del material de los tubos de acero inoxidable 904L suele ser de dos a tres veces superior al del 316L. Además, el alto contenido en níquel del 904L provoca una mala conductividad térmica y un alto coeficiente de dilatación térmica. Se requiere un control más estricto del proceso durante el mecanizado y la soldadura; de lo contrario, es probable que se produzcan grietas en caliente. Se utiliza exclusivamente en determinados entornos de corrosión extrema.
No.El 904L es un acero inoxidable austenítico, y su microestructura interna no sufre transformación de fase durante el calentamiento y el enfriamiento. El único propósito del tratamiento térmico de las tuberías 904L es aliviar las tensiones de trabajo en frío y disolver los precipitados dañinos, restaurando así completamente su óptima resistencia a la corrosión.